▎ 摘　　要

Membranes assembled by two-dimensional (2D) nanosheets have high potential for advanced molecular separation. The intercalation of nanomaterials into the laminar membrane is a promising strategy to control the nanochannel structure. We present 2D niobate nanosheet (NbN)-Graphene oxide (GO) composite membranes fabricated by simple vacuum filtration. The effect of the weight ratio of NbN/GO on the membrane structures and performances is investigated. The NbN-rich membranes have a more stable structure in the wet condition and a membrane structure with a larger channel size compared with GO-rich membranes. Especially, NbN55-GO45 (weight ratio of NbN/GO = 55/45) shows a superior water permeability of 20 L m(-2) h(-1) bar(-1), which is around 6 times higher than an NbN membrane (NbN100) and 2 times higher than a GO membrane (GO100), while maintaining good rejection abilities of an anionic dye (nearly 100% for Evans blue) and salt (60% for Na2SO4). Different models for the water pathway through nanochannels can be classified according to the composite ratio of the NbN-GO membranes.