▎ 摘　　要

A graphene-based or carbon-based aerogel is a three-dimensional (3D) solid material in which the carbon atoms are arranged in a sheet-like nanostructure. In this study, we report the synthesis of low-density polymer-modified aerogel monoliths by 3D macroassemblies of graphene oxide sheets that exhibit significant internal surface areas (982 m(2)/g) and high electrical conductivity (similar to 0.1 to 1 x 10(2) S/cm). Different types of materials were prepared to obtain a single monolithic solid starting from a suspension of single-layer graphene oxide (GO) sheets and a polymer, made from the precursors 4-carboxybenzaldehyde and poly(vinyl alcohol). These materials were used to cross-link the individual sheets by covalent bonds, resulting in wet-gels that were supercritically dried and then, in some cases, thermally reduced to yield graphene aerogel composites. The average densities were approaching 15-20 mg/cm(3). This approach allowed for the modulation of the distance between the sheets, pore dimension, surface area, and related properties. This specific GO/polymer ratio has suitable malleability, making it a viable conductive material for use in 3D printing; it also has other properties suitable for energy storage, catalysis, sensing and biosensing applications, bioelectronics, and superconductors.