▎ 摘　　要

Microbial fuel cell (MFC) is a combined technology for simultaneous generation of electricity and wastewater treatment. In MFC, the proton exchange membrane (PEM) is an essential component affecting electricity generation. In the current study, two proton exchange membranes, namely sulfonated polyethersulfone (SPES) and graphene oxide/sulfonated -polyethersulfone hybrid nanocomposite (GO-SPES), were prepared and characterized using Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). The collected information confirmed the successful preparation of the membranes. Moreover, contact angle measurements, ion exchange capacity and degree of sulfonation of the prepared membranes were determined. The results showed that the introduction of GO nanoparticles into SPES membrane improved its proton exchange capability and resulted in better performance. The power density and the current generated from SPES membrane were 60 mW/m(2) and 425 mA/m(2), respectively. For GO-SPES, the obtained power density was 101.2 mW/m(2) and the current was 613 mA/m(2). Both membranes showed comparable chemical oxygen demand (COD) removal efficiency of about 80%; suggesting that the prepared membranes are working efficiently in wastewater treatment as PEMs in MFCs. As a final point, the performance of GO-SPES membrane was compared to the performance of the well-known Nafion (R) 117 membrane and the results were promising. To conclude, the GO-SPES membrane is an outstanding membrane for use as PEM in MFCs for simultaneous generation of electricity and wastewater treatment.