We report a simple and effective approach for high performance PbZr0.52Ti0.48O3 (PZT) based flexible and semi-transparent NGs that exploit the electrical, mechanical and transparent properties of graphene. PZT NGs are successfully demonstrated for continuous driving of a liquid crystal display screen and a light emitting diode. A good quality PZT film was deposited on Pt/Ti/SiO2/Si wafer by the sol-gel method, exhibiting a typical hysteresis loop in the low voltage region. A graphene film was used in the interdigitated electrode form to improve the PZT/graphene interface under mechanical stress. Further improvement in NGs performance was realized by p-type doping in graphene, resulting in an increase in current density. NGs showed a high output voltage similar to 2 V, current density similar to 2.2 mu A cm(-2) and power density similar to 88 mW cm(-3) at an applying force of 0.9 kgf. This can efficiently run commercially available electronic components in a self-powered mode, without any external electrical supply.