▎ 摘　　要

Carbon fibre-phenolic matrix (CF-P) composites containing graphene nanoplatelets (GNPs) were manufactured for improved mechanical and thermal properties. For comparison, micrometer-size pyrolytic graphite powder (GP) was also incorporated in CF-P composites. The loading of carbon fibres was kept constant at 60 wt-% while the quantity of GNPs was varied from 0.1 wt-% to 0.3 wt-% and GP from 1.0 wt-% to 3.0 wt-%. Only GNPs were functionalised by ultraviolet-ozone treatment to improve their dispersion in the matrix while all the composites were manufactured by hand layup method and characterised by scanning electron microscopy, impact, flexural, thermogravimetry and ablation tests. The composite containing 0.3 wt-% GNPs showed considerable improvement in ablation, flexural and impact testing as compared to CF-P composites containing GP. Finally, the ablation mechanisms of post-ablated composites were discussed in the light of available data in the literature.