▎ 摘　　要

In order to prepare novel fluorocarbon resin coatings with outstanding wear and corrosion resistance, this manuscript prepared few-layer fluorinated graphene (FG) nanosheets through a simple mechanical exfoliation method, and nanofilled them into the fluoro-carbon resin/epoxy resin (FEVE/EP) blended matrix to prepare FG-FEVE/EP nanocomposite coating. The exfoliated FG was 4-7 layers and contained active O-H and C=C functional groups in addition to abundance of C-F bonds that were identical to those of FEVE. The as -prepared FG layers were freely stacked and possessed low orientation, and exhibited good dispersion and interfacial compatibility in the FEVE/EP matrix. The FG-FEVE/EP nano -composite coating filled with 0.1 wt% FG (0.1% FG-FEVE/EP) achieved the hardness of 3H and adhesion strength of 7.7 MPa. Compared with pure FEVE/EP coating, the 0.1% FG-FEVE/ EP reduced the friction coefficient by 10.6% and 30.7% and the wear rate by 55.1% and 56.1% under dry friction and simulated seawater friction conditions, respectively. In addition, the EIS testing and fitting data yielded that the impedance modulus of the 0.1% FG-FEVE/EP was two orders of magnitude higher than that of the FEVE/EP coating after 15 days of immer-sion in NaCl solution, and the coating resistance (R-c) still reached 1.6 x 10(9) omega cm(2), showing excellent corrosion resistance. The excellent wear and corrosion resistance of the FG-FEVE/ EP was attributed to the fact that the FG prepared by mechanical peeling was uniformly dispersed and interfacially compatible in the FEVE/EP matrix, which contributed to the excellent interlayer lubrication, stress resistance and barrier corrosion protection of FG. (C) 2022 The Author(s). Published by Elsevier B.V.