▎ 摘　　要

In this paper, we report single layer graphene (SLG) hybridized with silver nanoplates, in which nanoplates act as either a charge doping or a field enhancement source for the SLG Raman spectrum. Surprisingly, the stiffening of both G and 2D peaks of more than 10 cm(-1) was observed with no plasmonic enhancement of peaks, indicating that p-doping from nanoplates on SLG is occurring. Such observation is explained in terms of the contact separation distance between the graphene and the silver nanoplates being enough (similar to 4 angstrom) to cause a Fermi level shift in graphene to allow p-doping. When nanoplates were modified in shape with laser irradiation by either photothermal plasmon printing or laser induced ablation, the charge doping was lifted and the strong plasmonic enhancement of Raman signals was observed, indicating that the separation distance is increased. Further, when the nanoplates are oxidized, the two effects on the Raman bands of SLG are turned off, returning the Raman signals back to the original SLG state. Published by AIP Publishing.