▎ 摘　　要

Multifunctional electrocatalyst enabled electrochemical hydrogen/oxygen redox plays pivotal roles in variable energy conversion/storage devices and some coupling devices. The daunting challenge in developing multifunctional electrocatalysts at present is to effectively incorporate multiple active sites into one material. Herein, we presented a general protocol by a controllable pyrolysis/vapor reforming process, which allows for reconstitution to form CoNC nano-units, while preserving Co and Co oxides simultaneously. The material by co-intercalation of these active units into graphene generates outstanding trifunctional activities. The overpotentials for hydrogen and oxygen evolution reactions are 205 and 360 mV (at 10 mA cm(-2)), respectively, and the half-wave potential for the oxygen reduction reaction is 0.81 V, outperforming most of the state-of-the-art trifunctional electrocatalysts. A maximum power density of 23 mW cm(-2) and 1000 stable cycles were realized in the as-prepared material equipped Zn-air battery. This battery further drove overall water splitting for 24 hours, at a faradaic efficiency of ca. 100% and gas production rate of 0.035 and 0.017 mL min(-1) for hydrogen and oxygen, respectively. Thus this work offers a general approach to explore other efficient multifunctional electrocatalysts for application in renewable energy technologies.