▎ 摘　　要

Low-dimensional nanoparticles have a strong ability to induce the crystallization of polymer matrices. One-dimensional carbon nanotubes (CNTs) and two-dimensional graphene nanosheets (GNSs), both of which are both carbon-based nanoparticles, provide a good opportunity to investigate the effects of differently dimensional nanoparticles on the crystallization behavior of a polymer. For this purpose, respective nanocomposites of CNTs and GNSs with poly(L-lactide) (PLLA) as matrix were prepared by solution coagulation. Time-resolved Fourier-transform infrared spectroscopy (FTIR) and synchrotron wide-angle X-ray diffraction (WAXD) were performed to probe chain conformational changes and to determine the crystallization kinetics during the isothermal crystallization of the PLLA nanocomposites and neat PLLA, especially in the early stages. Both CNTs and GNSs could serve as nucleating agents in accelerating the crystallization kinetics of PLLA: however, the ability of CNTs to induce crystallization was stronger than that of GNSs. On increasing the content of CNTs from 0.05 to 0.1 wt %, the induction period was shortened and the crystallization rate was enhanced, hut the reverse situation was found for GNSs nanocomposites. In the case of neat PLLA, -CH3 interchain interactions preceded -(COC + CH3) interchain interactions during the crystallization. Conversely, in the CNTs and GNSs nanocomposites, the conformational ordering began with -(COC + CH3) interchain interactions, which resulted directly in a reduced induction period. Interchain interactions of this type could be explained in terms of surface-induced conformational order (SICO). Finally, the effect of the dimensionality of the nanoparticles on the crystallization behavior of PLLA is discussed.