▎ 摘　　要

Lithium (Li) metal has long been considered the "holy grail" of battery anode chemistry but is plagued by low efficiency and poor safety due to its high chemical reactivity and large volume fluctuation, respectively. Here we introduce a new host of wrinkled graphene cage (WGC) for Li metal. Different from recently reported amorphous carbon spheres, WGC show highly improved mechanical stability, better Li ion conductivity, and excellent solid electrolyte interphase (SEI) for continuous robust Li metal protection. At low areal capacities, Li metal is preferentially deposited inside the graphene cage. Cryogenic electron microscopy characterization shows that a uniform and stable SEI forms on the WGC surface that can shield the Li metal from direct exposure to electrolyte. With increased areal capacities, Li metal is plated densely and homogeneously into the outer pore spaces between graphene cages with no dendrite growth or volume change. As a result, a high Coulombic efficiency (CE) of similar to 98.0% was achieved under 0.5 mA/cm(2) and 1-10 mAh/cm(2) in commercial carbonate electrolytes, and a CE of 99.1% was realized with high-concentration electrolytes under 0.5 mA/cm(2) and 3 mAh/cm(2). Full cells using WGC electrodes with prestored Li paired with Li iron phosphate showed greatly improved cycle lifetime. With 10 mAh/cm(2) Li metal deposition, the WGC/Li composite anode was able to provide a high specific capacity of similar to 2785 mAh/g. With its roll-to-roll compatible fabrication procedure, WGC serves as a highly promising material for the practical realization of Li metal anodes in next-generation high energy density secondary batteries.