• 文献标题:   Rapid growth of large-area single-crystal graphene film by seamless stitching using resolidified copper foil on a molybdenum substrate
  • 文献类型:   Article
  • 作  者:   CHENG Y, BI H, CHE XL, ZHAO W, LI DZ, HUANG FQ
  • 作者关键词:  
  • 出版物名称:   JOURNAL OF MATERIALS CHEMISTRY A
  • ISSN:   2050-7488 EI 2050-7496
  • 通讯作者地址:   Chinese Acad Sci
  • 被引频次:   2
  • DOI:   10.1039/c9ta05483a
  • 出版年:   2019

▎ 摘  要

Graphene grain boundaries are inevitably formed during the stitching of graphene domains, consequently degrading the graphene film quality. Herein, we have developed a new strategy to grow large-area single-crystal graphene film using resolidified Cu foil on a Mo substrate. The Cu foil resolidifies into a quasi-atomically smooth Cu film, and recrystallizes into a single-crystal Cu (111) film sticking to the Mo foil surface after annealing above the Cu melting point under a H-2 atmosphere. A single-crystal graphene film of more than 2 inches in size is obtained by seamless stitching of more than 99% ultra-highly oriented single-crystal graphene domains of similar to 500 mu m on the resolidified Cu (111) surface, and it shows a low average sheet resistance of 315 omega sq(-1) and a high optical transmittance of similar to 97.6%. Moreover, the field-effect mobility of the single-crystal graphene film reaches up to 11 500 cm(2) V-1 s(-1), significantly higher than that of polycrystalline graphene film (similar to 4260 cm(2) V-1 s(-1)). This approach can easily be scaled up to achieve large-area and high-quality graphene film with a single crystal nature, and thereby realize various industrial-level applications at low cost.