▎ 摘　　要

This study loaded Bi/Bi2O3 on the surface of reduced graphene oxide (rGO) to perform a two-step facile synthesis of rGO@Bi/Bi2O3 as a bismuth-based nanocomposite. First, Bi/Bi2O3 nanocomposites were synthesised via a solvothermal process using Bi(NO3)(3) 5H(2)O as the Bi3+ precursor and dimethyl sulfoxide (DMSO) as the solvent. Second, we exfoliated rGO in water to functionalise Bi/Bi2O3 with a few layers of rGO. Obtained nanocomposites were characterised with scanning electron microscopy and X-ray diffraction. We also measured the nanocomposites' photocatalytic activity using cationic dyes, specifically methylene blue (MB) and rhodamine B (RhB). Additionally, ultraviolet-visible spectroscopy was used to determine the optical properties of rGO@Bi/Bi2O3. Photodegradation was recorded under differing durations of exposure to visible light. Reaction rates were recorded at 14.6 x 10(-4) min(-1) and 22.2 x 10(-3 )min(-1) for MB and RhB, respectively, while photodegradation efficiency was logged at 17% and 81%.