▎ 摘　　要

We report nanocrystalline carbon impurities coexisting with graphene synthesized via chemical vapor deposition on platinum. For certain growth conditions, we observe micron-size island-like impurity layers which can be mistaken for second graphene layers in optical microscopy or scanning electron microscopy. The island orientation depends on the crystalline orientation of the Pt, as shown by electron backscatter diffraction, indicating growth of carbon at the platinum surface below graphene. Dark-field transmission electron microscopy indicates that in addition to uniform single-crystal graphene, our sample is decorated with nanocrystalline carbon impurities with a spatially inhomogeneous distribution. The impurity concentration can be reduced significantly by lowering the growth temperature. Raman spectra show a large D peak, however, electrical characterization shows high mobility (similar to 8000 cm(2)/Vs), indicating a limitation for Raman spectroscopy in characterizing the electronic quality of graphene. (C) 2014 AIP Publishing LLC.