▎ 摘　　要

The reduced graphene oxide (rGO) aerogels are particularly attractive owing to their ultralight-weight, high surface area and interconnected macroporosity for energy storage applications. However, pure rGO aerogels are generally weak and brittle to limit their practical applications. To overcome this drawback, a small amount of synthetic dopamine-conjugated poly(aspartic acid) was mixed with graphene oxide to fabricate ultralight rGO aerogels with high porosity and mechanical integrity via hydrothermal reactions at 80 degrees C and freeze-drying process. In addition, the Fe3+ ionic species was chosen for an additional cross-linker to further strengthen the ultralight poly(aspartic acid/dopamine) functionalized rGO aerogel, abbreviation for PAAD/rGO, through the coordination bonding between Fe3+ and carboxylic acid or catechol groups of both polymer and rGO sheets at pH 9 (PAAD/rGO-Fe?). The hybrid electrodes of PAAD/rGO-Fe? showed the reversible transformation of the Fe3+ tris-catecholate complexes into mono-catecholate promoting Quinone (Q)-hydroquinone (QH(2)) in 1.0molL(-1) H2SO4 electrolyte, thus delivering a high specific capacitance of 276.4Fg(-1) at 0.5Ag(-1) and capacitance retention of 88.2% after 5000 cycles. Moreover, this compressible aerogel provided high strength with 150kPa without noticeable structural fracture after 80% compression and repeated deformation processes suggesting applications in energy storage and absorption.