▎ 摘　　要

LiNi1/3Co1/3Mn1/3O2 cathode coated with a thin layer of graphene (similar to 8 nm) is successfully synthesized by self-assembly and pyrolysis of polyelectrolyte layers on the surface of NMC particles. The graphene coated NMCs still possess a layered structure with good crystallinity and demonstrate a superior electrochemical performance (e.g., rate capability and cycling stability). The best graphene coated NMC cathode is prepared at a calcination temperature of 800 degrees C, exhibiting a capacity retention of similar to 90% vs. 78% for pristine NMC @ cycle 100 and 1 C rate. The improvement in cycling performance is further enlarged after 500 cycles (74% vs. 51%). This can be attributed to the dual functions of graphene coating in enhancing electronic conductivity and protecting NMC surface from the contact with electrolyte during the electrochemical reaction.