The graphene/polyurethane (GN@PU) sponge was prepared via simple dip-coating PU sponges in graphene aqueous suspension containing cellulose nanowhiskers (CNWs), where CNWs played a vital role to facilitate the uniform graphene sheets coated on the skeletons of polyurethane sponge (PU). The super-hydrophobic GN@PU sponge was obtained by optimizing the ratio of GN and CNWs to choose the final coating suspensions of GN/CNWs mixture or pure graphene. The GN@PU sponge showed densely packed graphene sheets, contributing super-hydrophobicity to the sponge with water contact angle of 152. and a large lubricating oil absorption value of 31 g g(-1). The elasticity, mechanical durability, thermal and chemical stability were all found to be improved after coating with the thin GN layers. Moreover, the GN@PU sponges possess outstanding recyclability and stability since no decline in absorption efficiency was observed after more than 100 cycles. (C) 2017 Elsevier B.V. All rights reserved.