▎ 摘　　要

Polyamide 11/graphene coatings were prepared through a spraying method with as-prepared organophilic graphene. The tribological results showed that the wear life of composite coatings was obviously higher than that of neat Polyamide 11 coating; however, the values of friction coefficients had hardly changed. The optimal content of graphene in the range of our experiments was 0.4 wt%, and the wear life of the composite coating increased by 460%-880% compared with that of pristine Polyamide 11 coating. The morphology of worn surface for both pristine Polyamide 11 and the composites coatings was studied, and the wear mechanisms were discussed.