▎ 摘　　要

Excellent mechanical and electrical properties of graphene-based paper-like materials are essential for applications in flexible conductors, energy-storage devices, etc. The graphene oxide (GO) supernatant separated by centrifugation and ultrasonication has been used to prepare graphene oxide paper and reduced graphene oxide paper (rGOP) with high strength and conductivity. However, this method has cumbersome steps and low supernatant concentration, which greatly increases time and energy consumption, and is not suitable for rapid batch preparation of high-strength and high-thickness rGOP. Herein, a high-speed mechanical shearing method has been used to efficiently exfoliate graphite oxide suspension into high-concentration GO slurry with large lateral size, and rGOP has been further prepared by blade coating and HI acid chemical reduction. Compared with the product prepared by ultrasonic exfoliation method, the average area of GO sheets obtained via the mechanical shear exfoliation method can reach around 16.31 mu m(2). As a result, the mechanical properties and conductivity of the prepared rGOP have been increased by 30% and 23.5%, respectively, with the tensile strength and electrical conductivity of 478.2 MPa and 208.4 S/cm being obtained. The developed method is of great significance for the large-scale production and emerging applications of lightweight and high-performance rGOP. [GRAPHICS]