▎ 摘　　要

This investigation studies TiB2-SiC-graphene ceramics in terms of microstructure and mechanical properties. Spark plasma sintering (SPS) at 1800 ? was employed as manufacturing route, and the as-sintered composite was studied using high-resolution transmission electron microscopy (HRTEM), field emission scanning electron microscopy (FESEM), X-ray photoelectron spectroscopy (XPS), energy-dispersive X-ray spectroscopy (EDS), X Ray diffractometry (XRD), and nano-indentation. The system was found to be unreactive, and all results dismissed the in-situ nucleation of B4C and TiC phases. Although TiO2 and B2O3 surface impurities were mainly reduced upon the incorporation of graphene nano-platelets (GNPs), the presence of SiO2 in the final microstructure was confirmed by both XRD and HRTEM methods. The TiB2 phase achieved a hardness of 35 GPa and a Young modulus of 539 GPa, which were roughly 45% and 25% higher than those measured for the SiC phase.