A superparamagnetic reduced graphene oxide-Fe3O4 hybrid composite (rGO-Fe3O4) was prepared via a facile and straightforward method through the solvothermal reaction of iron (III) acetylacetonate (Fe(acac)(3)) and graphene oxide (GO) in ethylenediamine (EDA) and water. By this method, chemical reduction of GO as well as the formation of Fe3O4 nanoparticles (NPs) can be achieved in one step. The Fe3O4 NPs are firmly deposited on the surfaces of rGO, avoiding their reassembly to graphite. The rGO sheets prevent the agglomeration of Fe3O4 NPs and enable a uniform dispersion of these metal oxide particles. The size distribution and coverage density of Fe3O4 NPs deposited on rGO can be controlled by varying the initial mass ratio of GO and iron precursor, Fe(acac)(3). With an initial mass ratio of GO and Fe(acac)(3) of 5:5, the surfaces of rGO sheets are densely covered by spherical Fe3O4 NPs with an average size of 19.9 nm. The magnetic-functionalized rGO hybrid exhibits a good magnetic property and the specific saturation magnetization (M-S) is 13.2 emu g(-1). The adsorption test of methylene blue from aqueous solution demonstrates the potential application of this rGO-Fe3O4 hybrid composite in removing organic dyes from polluted water.