▎ 摘　　要

Flexible all-solid-state supercapacitors (SCs) have great potential applications in flexible and wearable electronics because of their safety, high power density, flexibility, and portability. Herein, a self-supported film electrode comprising nitrogen-doped reduced graphene oxide intertwined with vanadium trioxide nanoflakes (V2O3/N-rGO) was fabricated. The V2O3 nanoflakes have abundant active sites accessible to charge storage, and nitrogen-doped reduced graphene oxide provides a flexible support. The V2O3/N-rGO film electrodes exhibit high conductivity, short diffusion length for ions and electrons, and robust flexibility, resulting in excellent capacitive properties and flexibility. The flexible V2O3/N-rGO film electrode has a high areal capacitance of 216 mF cm(-2) at a current density of 1 mA cm(-2). All-solid-state flexible SCs assembled by sandwiching two self-supported V2O3/N-rGO hybrid electrodes with alkaline poly(vinyl alcohol) (PVA) and LiCl gel electrolyte show an ideal volumetric capacitance of 8.1 F cm(-3), an energy density of 0.55 mW h cm(-3), and a power density of 0.035 W cm(-3) at a current density of 0.1 A cm(-3), based on the entire cell. This indicates that the self-supported V2O3/N-rGO film electrodes have great potential applications in portable and wearable flexible electronics due to their high capacitance, high energy/power density, and good mechanical flexibility.