This research study used metakaolin as a raw material, a mixed solution of sodium hydroxide and sodium silicate as an alkali excitant, and a graphene dispersant as an additive to manufacture a graphene geopolymer sample. The compressive strength and bending strength of the sample were tested. The results showed that the geopolymer hydration products were observed to be more compact, and the internal porosity was reduced after the addition of the graphene. The geopolymer strengths had been obviously increased, and the compressive strength and bending strength reached 46.9MPa and 6.7MPa, respectively. However, the graphene's role in improving the strength of the original geopolymer became gradually weakened when the addition amounts of the graphene were increased to a certain extent. Furthermore, the role of the graphene in improving the compressive strength of the geopolymer was determined to gradually decrease with the increase in the content of sodium hydroxide in the alkali excitant. (C) 2018 Author(s).