▎ 摘　　要

In this study, compact urea-formaldehyde microcapsules containing paraffin (UFP) phase change materials (PCMs) were prepared via in situ polymerisation. The thermal conductivity of the PCMs was enhanced without influencing their enthalpy by adding graphene oxide (GO). Two modification methods were investigated: One in which GO is added to the inside of microcapsules, defined as "paraffin/GO@UF composite"; and another in which GO is coated onto the surface of shell, defined as "paraffin@UF/GO composite". The GO sheets were visible in scanning electron microscope (SEM) images of paraffin@UF/GO composite. The thermal conductivity was 0.2236 +/- 0.0003 W/(mK) for UFP particles, was 0.2517 +/- 0.0003 W/(mK) for the paraffin/GO@UF composite (10wt%), and was 1.0670 +/- 0.0020 W/(mK) for paraffin@UF/GO composite (10wt%), respectively. The encapsulation efficiency of all samples exceeded 80% (w/w) and all samples exhibited favourable thermal stability and reliability. The IR emissivity of paraffin@UF/GO was lower than that of paraffin/GO@UF when the same GO amount was added to the composite.