▎ 摘　　要

A simple solvothermal method was used to prepare self-assembled V2O5 nanosheets/reduced graphene oxide (RGO) hierarchical nanocomposite. In this nanocomposite, the V2O5 nanosheets assembling on the RGO constitute a 3-D hierarchical nanostructure with high specific surface area and good electronic/ionic conducting path. When used as the cathode materials, the V2O5 nanosheets/RGO nanocomposites exhibit highly reversible capacity and good rate capability relative to the bulk material. The V2O5 nanosheets/RGO nanocomposite anode was able to charge/discharge at high current densities of 3000 mA g(-1) (10 C), 6000 mA g(-1) (20 C) and 15 A g(-1) (50 C), with discharge capacities of approximately 138, 112 and 76 mA h g(-1), respectively. Meanwhile, a discharge capacity of 102 mA h g(-1) can be delivered after 160 cycles at 2 C, showing a good cycling stability. The improved performance could be attributed to the enhanced electron transport and Li+ diffusion that results from the hierarchical nanostructure of V2O5 nanosheets/RGO nanocomposites.