▎ 摘　　要

SiOx suffers from the 200% volume change during cycling and low electronic conductivity, resulting in poor cyclability and rate capability as a lithium-ion battery anode. Herein, we demonstrate a dopamine polymerization-guided carbon coating for SiOx anodes (SiOx@PDA@GNH). SiOx@PDA@GNH delivers charge capacities of 1269 and 1140 mA h.g(-1) at charge rates of 0.05 and 3 C, respectively, and a capacity retention of 79.60% after 150 cycles at 1 C. A full cell with LiNi0.8Co0.1Mn0.1O2 or cathode demonstrates a capacity retention of >80% after 100 cycles at the rate of 0.33 C with an area capacity over 3.2 mA h.cm(-2). Suppressed crack and overgrowth of the SEI layer are the key contributions for the improved performance. These results enlighten a practical pathway for the designing and modifications of SiOx anodes for high energy density lithium-ion batteries.