▎ 摘　　要

A simple and effective transparent conducting electrodes (TCEs) based on reduced graphene oxide film embedded with silver nanowire- (AgNW-rGO) was developed. The AgNW-rGO hybrid electrode was fabricated by using a simple and scalable dip-coating method. This solution processed TCEs showed high electrical conductivity when compared with pristine AgNW. AgNW-rGO TCEs also exhibited better stability than the pristine AgNW film when exposed to the ambient atmosphere. The electrical conductivity is found to increase by 4-fold with increase in the number of dipping cycles of AgNW after coating the graphene oxide (GO). This increase in the observed conductivity is attributed to the gas-barrier property of GO. AgNWirGO TCEs exhibited a sheet resistance of 27 Omega/square with transparency=72% at 550 nm. (C) 2014 Elsevier B.V. All rights reserved.