▎ 摘　　要

Graphene/carbon composite films were prepared by electrospraying a graphene/polyacrylonitrile composite solution on SiO2-coated silicon substrates and subsequent heat treatment. The as-produced graphene/carbon composite films had a porous structure comprising graphene layers. With a magnetic field applied perpendicularly to the sample, an unexpectedly significant positive magnetoresistance attributed to e-e interaction and weak localization has been observed, which constantly increases with the magnetic field in the temperature range of 300-50 K from 0 to 80 kOe.