▎ 摘　　要

Na-ion capacitors (NICs) and Na-based dual-ion batteries (Na-DIBs) have been considered to be promising alternatives to traditional lithium-ion batteries (LIBs) because of the abundance and low cost of the Na-ion, but their energy density, power density and life cycle are limited. Herein, dual-vacancy (including K+ and F- vacancies) perovskite fluoride K0.86MnF2.69@reduced graphene oxide (rGO; recorded as Mn-G) as anode for NICs and Na-DIBs has been developed. The special conversion/intercalation dual Na-ion energy storage mechanism and pseudocapacitive dynamics are analyzed in detail. The Mn-G//AC NICs and Mn-G//KS6 Na-DIBs delivered a maximum energy density of 92.7 and 187.6 W h kg(-1), a maximum power density of 20.2 and 21.12 kW kg(-1), and long cycle performance of 61.3 and 68.4 % after 1000 cycles at 5 A g(-1), respectively. Moreover, Mn-G//AC NICs and Mn-G//KS6 Na-DIBs can work well over a wide range of temperatures (-20 to 40 degrees C). These results make it competitive in Na-ion storage applications with high energy/power density over a wide temperature range.