▎ 摘　　要

This work consists of studying the influence of two thermally reduced graphene oxides (TRGOs), containing oxygen levels of 15.8% and 8.9%, as fillers on the barrier properties of thermoplastic polyurethane (TPU) nanocomposites prepared by melt-mixing processes. The oxygen contents of the TRGOs were obtained by carrying out the thermal reduction of graphene oxide (GO) at 600 degrees C and 1000 degrees C, respectively. The presence and contents of oxygen in the TRGO samples were determined by XPS and their structural differences were determined by using X-ray diffraction analysis and Raman spectroscopy. In spite of the decrease of the elongation at break of the nanocomposites, the Young modulus was increased by up to 320% with the addition of TRGO. The barrier properties of the nanocomposites were enhanced as was evidenced by the decrease of the permeability to oxygen, which reached levels as low as -46.1%.