▎ 摘　　要

Graphene oxide functionalized by diethylenetriamine (DETA) was prepared and characterized with SEM, XRD, BET, TGA and IR spectroscopy techniques to find out its morphology, crystalline building, porous structure, thermal stability and functional groups. The CO2 solubility in 40 wt% aqueous amine solution, 40 wt% aqueous amine solution +0.1 wt% GO, and 40 wt% aqueous amine solution +0.1 wt% DETA-GO is determined. The solubility measurements were performed at three temperature (303.15, 313.15 and 323.15 K) and CO2 partial pressures up to 2200 kPa. Addition of GO and DETA-GO to MDEA (N-Methyldiethanolamine) solution enhanced the CO2 adsorption capacity of the aqueous amine solution up to 7.5% and 12.5%, respectively. Increasing CO2 partial pressure and decreasing temperature enhanced the CO2 solubility.