• 文献标题:   Structural and Morphological Studies of Bi2O3/MWCNTs Doped Reduced Graphene Oxide for Energy Storage Applications
  • 文献类型:   Article
  • 作  者:   SUREKHA G, RAVI N, SUVARNA RP, KRISHNAIAH KV
  • 作者关键词:  
  • 出版物名称:   ECS JOURNAL OF SOLID STATE SCIENCE TECHNOLOGY
  • ISSN:   2162-8769 EI 2162-8777
  • 通讯作者地址:  
  • 被引频次:   2
  • DOI:   10.1149/2162-8777/ac5eb5
  • 出版年:   2022

▎ 摘  要

Bismuth oxide (Bi2O3), multi-wall carbon nanotubes (MWCNTs), reduced graphene oxide (rGO) and its composite were synthesized by modified Hummers method followed by chemical and thermal reduction processes. During synthesis, graphene oxide (GO) was reduced to rGO and decorated evenly with Bi2O3 and CNTs. Average crystallite size of graphite flakes (GF), GO, rGO, rGO/Bi2O3, rGO/CNTs and rGO/Bi2O3/CNTs is calculated from XRD profiles using the Scherer equation are 77.75, 11.91, 1.79, 18.1, 21.05 and 18.05 nm, respectively. In XRD, deconvolution of rGO/Bi2O3/CNTs, C-60 and C-70 diffraction peaks were observed. The morphology of rGO/Bi2O3/CNTs have smoother surface similar to GO, rGO, rGO/Bi2O3 and rGO/CNTs except GF, was revealed in SEM images. HR-TEM analysis revealed carbon (002) in rGO with d-spacing of 0.34 nm, Bi (102) with d-spacing of 0.31 nm and MWCNTs on 2 nm scale. Bonding of Bi2O3 and CNTs with graphene layers led to the formation of novel functionalized nanocomposite which enhances electrical conductivity of rGO. Using AFM images of rGO/CNTs films thicknesses, arithmetic mean and RMS roughness were estimated as 6 nm at 14.91 nm and 19.27 nm, respectively. Results of rGO/Bi2O3/CNTs revealed that with the small crystallite size, functionalization and nanoscale roughness could be promising for energy storage applications.