▎ 摘　　要

Heteroatom doping of nanoc- arbon films can efficiently boost the pseudocapacitance of micro-supercapacitors (MSCs); however, wafer-scale fabrication of sulfur-doped graphene films with a tailored thickness and homogeneous doping for MSCs remains a great challenge. Here we demonstrate the bottom-up fabrication of continuous, uniform, and ultrathin sulfur-doped graphene (SG) films, derived from the peripherical trisulfur-annulated hexa-peri-hexabenzocoronene (SHBC), for ultrahigh rate MSCs (SG-MSCs) with landmark volumetric capacitance. The SG filrn was prepared by thermal annealing of the spray-coated SHBC-based film, with assistance of a thin Au protecting layer, at 800 degrees C for 30 min. SHBC with 12 phenylthio groups decorated at the periphery is critical as a precursor for the formation of the continuous and ultrathin SG film, with a uniform thickness of similar to 10.0 nm. Notably, the as-produced all-solid-state planar SG-MSCs exhibited a highly stable pseudocapacitive behavior with a volumetric capacitance of similar to 582 F cm(-3) at 10 mV s(-1), excellent rate capability with a remarkable capacitance of 8.1 F cm(-3) even at an ultrahigh rate of 2000 V s(-1), ultrafast frequency response with a short time constant of 0.26 ms, and ultrahigh power density of similar to 1191 W cm(-3). It is noteworthy that these values obtained are among the best values for carbon-based MSCs reported to date.