▎ 摘　　要

Graphene sheets with different oxygen contents were prepared to functionalize the electrically insulating polymethylmethacrylate (PMMA). The influences of surface chemistry of graphene on rheological, electrical and electromagnetic interference (EMI) shielding properties of its PMMA composites were investigated. The appearance of frequency-independent storage modulus at low frequency suggests a solid-like viscoelastic behavior and the formation of an interconnected network of graphene in the matrix. Due to the favorable interfacial interactions arising from polarity matching, the graphene with a C/O ratio of 13.2 (graphene-13.2) shows a better dispersion in PMMA than those with lower C/O ratios, and thus its PMMA composites exhibit lower rheological and electrical percolation thresholds. The EMI shielding properties of the graphene/PMMA composites exhibit similar dependence on the oxygen content of graphene. A high EMI shielding effectiveness of similar to 30 dB was obtained for the PMMA composite with 4.2 vol.% of graphene-13.2 with microwave absorption as the dominant EMI shielding mechanism. (c) 2012 Elsevier Ltd. All rights reserved.