▎ 摘　　要

Crack propagation in graphene is essential to understand mechanical failure in 2D materials. We report systematic study of cracl propagation in graphene as a Function of defect content: Nanoindentations and subsequent images of graphene membranes with controlled induced defects show that while tears in pristine graphene span microns length, crack propagation is strongly reduced in the presence of defects. Accordingly, graphene oxide exhibits minor crack propagation. Our work suggests controlled defect creation as an approach to avoid catastrophic failure in graphene.