▎ 摘　　要

In this study, we report the energy-level-dependent Seebeck coefficients of thermally reduced graphene oxide (TrGO) measured using a field-effect transistor with a microheater. B-or N-doped TrGO samples were prepared using graphene oxide (GO) solutions containing 10 or 50 mM boric acid or urea. In addition, heavily N-doped TrGO was prepared by annealing GO under an Ar/NH3 atmosphere. During thermal annealing, boric acid and urea decomposed and B and N atoms were doped onto TrGO. The gate-dependent conductance of the samples was measured first. In general, all the samples exhibited ambipolar behavior. However, as a function of doping state, the gate-dependent conductance differed slightly in comparison with that of TrGO. B-TrGO exhibited more intensive hole transport, whereas N-TrGO exhibited more intensive electron transport. In addition, the conductance was investigated as a function of ambient temperature for evaluating bandgap opening by the doping effect. When the gate bias was changed from -80 to 80 V, the Seebeck coefficient of TrGO changed from 4 to -2 mV K-1, which indicates that the carrier transport was changed from hole to electron transport depending on the energy state. However, impurity-doped TrGO (B-or N-TrGO) exhibited different behaviors. The Seebeck coefficient of B-TrGO changed from 20 to -4 mV K-1, whereas that of N-TrGO changed from 4 to -10 mV K-1 in a similar range of gate bias. Notably, the Seebeck coefficient of heavily N-doped TrGO changed from -8 to -18 mV K-1 in a similar range of gate bias. On the basis of the Seebeck coefficients and relative bandgaps of TrGO, B-doped TrGO, and N-doped TrGO, the approximate relative electronic structure of TrGO was deduced.