▎ 摘　　要

We have obtained high pressure H-2 isotherms with respect to the interlayer distance of multilayered graphene oxide (GO) modulated by thermal annealing. The maximum storage capacity is 4.8 (0.5) wt% at 77 K (298 K) and at 9.0 MPa pressure. We found the optimum GO interlayer distance for maximum H2 uptake at 6.5 angstrom, similar to the predicted distances from first-principles calculations for graphite materials. Our results reveal that multilayered GO can be a practical material of choice to allow the use of graphene as a hydrogen storage material, provided that only small amounts of O and OH functional groups exist as spacers on GO sheets.