▎ 摘　　要

NOVELTY - Metalized graphene powder in the form of nickel-phosphorus graphene flakes obtained by metalization in which a nickel-phosphorus layer is applied by a chemical reduction process from a multicomponent metalizing solution containing 25-30 g/l nickel(II) sulfate, 16-30 g/l sodium hypophosphite, 10-35 g/l sodium acetate, and 20-30 cm3/l lactic acid to obtain a pH of 4.5 at 75-90 degrees C is disclosed. USE - Used as metalized graphene powder in the form of nickel-phosphorus graphene flakes. DETAILED DESCRIPTION - Metalized graphene powder in the form of nickel-phosphorus graphene flakes obtained by metalization in which a nickel-phosphorus layer is applied by a chemical reduction process from a multicomponent metalizing solution containing 25-30 g/l nickel(II) sulfate, 16-30 g/l sodium hypophosphite, 10-35 g/l sodium acetate, and 20-30 cm3/l lactic acid to obtain a pH of 4.5 at 75-90 degrees C is disclosed. The graphene flakes are activated prior to introduction into the metalizing solution with an activating solution containing 10 pts. wt. of ethanol and 1 pt. wt. of a solution prepared from 1 pt. wt. palladium chloride, 50 pts. wt. water, 11.8 pts. wt. hydrochloric acid and 118.5 pts. wt. ethanol.