• 专利标题:   Preparation of graphite anticorrosion coating by stirring modified graphene and silane modified epoxy resin, adding titanium dioxide and mica powder, stirring, and mixing with curing agent uniformly.
  • 专利号:   CN108546496-A
  • 发明人:   LIU J
  • 专利权人:   LENGINE TECHNOLOGY GROUP CO LTD
  • 国际专利分类:   C09D163/00, C09D005/08, C09D007/61, C09D007/62
  • 专利详细信息:   CN108546496-A 18 Sep 2018 C09D-163/00 201875 Pages: 6 Chinese
  • 申请详细信息:   CN108546496-A CN10424561 04 May 2018
  • 优先权号:   CN10424561

▎ 摘  要

NOVELTY - Preparation of graphite anticorrosion coating comprises adding modified graphene into silane modified epoxy resin, stirring, dispersing to obtain mixed resin, adding titanium dioxide and mica powder to mixed resin, stirring to obtain first component, mixing first component and curing agent uniformly to obtain graphite anticorrosion coating. The curing agent is diethylenetriamine. The mass ratio of first component and curing agent is 5:1-10:1. USE - Method for preparing graphite anticorrosion coating. ADVANTAGE - The coating has adhesion of 13 MPa, hardness of 8H, salt spray resistance of 10000 hours, heat resistance of 5000 hours, high temperature resistance of 1800 degrees C, UV aging of 4000 hours, impact resistance of 100 kg/m, sulfuric acid resistance of 1000 days, sodium hydroxide resistance of 1000 days, compactness of 0.65x 103 mg/cm2.day, solid content of more than 98%, no volatile organic compounds, and long-term environmental protection.