▎ 摘　　要

NOVELTY - A coating comprises base vinyl ester resin, 0.4-2 wt.% graphene dispersion and 3-5 wt.% vinyl ester resin curing agent. The base vinyl ester resin comprises 100 pts. wt. vinyl ester resin, 3-10 pts. wt. modifier, 0-50 pts. wt. water, 0.5-20 pts. wt. dispersant and 0.5-3 pts. wt. vinyl ester resin accelerator. Graphene dispersion comprises 20-60 pts. wt. graphene and 100 pts. wt. dispersant. USE - Coating. ADVANTAGE - The coating has excellent corrosion resistance, thermal conductivity, viscosity, rheological property, mechanical property, construction property, electrical property and electromagnetic property and high temperature resistance. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is included for preparation of coating, which involves adding 100 pts. wt. vinyl ester resin and modifier to reaction kettle, stirring at 40-60 degrees C for 1-1.5 hours, adding 0.5-2 pts. wt. dispersant, stirring for 10-20 minutes, adding vinyl ester resin accelerator, stirring for 5-10 minutes to obtain base vinyl ester resin, adding dispersant and 20-50 pts. wt. dried graphene powder to ultrasonic disperser, ultrasonically dispersing for 1-2.5 hours to obtain uniform and stable graphite dispersion, adding 100 pts. wt. base vinyl ester resin and graphene dispersion to high speed disperser, stirring at 1500-2000 rpm for 1-1.5 hours, dispersing, filtering, uniformly testing, packaging, adding vinyl ester resin curing agent and uniformly stirring.