▎ 摘　　要

NOVELTY - Flame retardant modified plastic comprises 30-60 pts. wt. acrylonitrile butadiene styrene (ABS), 5-12 pts. wt. polyester fiber, 4-10 pts. wt. nano aluminum hydroxide, 2-9 pts. wt. acetyl dibutyloctyl citrate, 2-4 pts. wt. nano titanium oxide, 2-4 pts. wt. nano zinc oxide, 1-3 pts. wt. nano calcium carbonate, 5-10 pts. wt. graphene, 4-12 pts. wt. white carbon black and 5-10 pts. wt. silane coupling agent. USE - The plastic is useful for automotive interior parts (claimed). ADVANTAGE - The plastic: has simple preparation method; excellent flame retardant; wear resistance; high-temperature resistance; and is environmentally friendly. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is also included for preparing flame retardant modified plastic comprising adding acrylonitrile butadiene styrene, polyester fiber, nano aluminum hydroxide, acetyl dibutyloctyl citrate, nano titanium oxide, nano zinc oxide, nano calcium carbonate, graphene, white carbon black and silane coupling agent and extruding at 180-220 degrees C to obtain the product.