• 专利标题:   Graphene elastic film used in conductive devices, comprises elastic film formed by cross-linking two graphene films having semispherical convex structure.
  • 专利号:   CN106185906-A, CN106185906-B
  • 发明人:   GAO C, PENG L, XU Z
  • 专利权人:   UNIV ZHEJIANG, UNIV ZHEJIANG
  • 国际专利分类:   C01B031/04, C01B032/182, C01B032/184
  • 专利详细信息:   CN106185906-A 07 Dec 2016 C01B-031/04 201723 Pages: 11 Chinese
  • 申请详细信息:   CN106185906-A CN10566947 15 Jul 2016
  • 优先权号:   CN10566947

▎ 摘  要

NOVELTY - The graphene elastic film comprises an elastic film formed by cross-linking two graphene films having semispherical convex structure. USE - Graphene elastic film used in conductive devices. ADVANTAGE - The graphene elastic film has excellent flexibility, repeated fold more than 100000 times without leaving a crease, good thermal conductive, elastic elongation at break 30-50%, electrical conductivity of 600-1000 seconds/cm. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is included for a method for preparing graphene elastic film, which involves: (A) dissolving 100 pts. wt. graphene oxide in water to prepare aqueous solution of graphene oxide having a concentration of 6-30 mg/ml; (B) adding 0.1-10 pts. wt. auxiliary agent under ultrasonic dispersion to give graphite oxide film; (C) drying the obtained graphite oxide film naturally; (D) reducing the dried graphite oxide film in hydroiodic acid solution; (E) placing the reduced graphite oxide film in ethanol at 40-90 degrees C for 5-10 minutes to wash out surface; and (F) drying naturally in air to obtain the graphene elastic film. DESCRIPTION OF DRAWING(S) - The drawing shows a schematic surface view of the graphene elastic film.