• 专利标题:   Preparing graphene anticorrosive paint for marine environment involves dispersing aniline monomer into 5-sulfosalicylic acid, ultrasonically processing for 20-40 minutes, adding graphene oxide aqueous solution, stirring for 20-40 minutes.
  • 专利号:   CN110157291-A
  • 发明人:   GUO W, LIU X
  • 专利权人:   AEROSPACE SCI IND DEFENSE TECHNOLOGY
  • 国际专利分类:   C09D163/00, C09D005/08, C09D007/61
  • 专利详细信息:   CN110157291-A 23 Aug 2019 C09D-163/00 201972 Pages: 7 Chinese
  • 申请详细信息:   CN110157291-A CN10306389 17 Apr 2019
  • 优先权号:   CN10306389

▎ 摘  要

NOVELTY - Preparing graphene anticorrosive paint for marine environment involves dispersing the aniline monomer into the 5-sulfosalicylic acid, ultrasonically processing for 20-40 minutes, adding graphene oxide aqueous solution, stirring for 20-40 minutes, performing ultrasonic dispersion for 20-40 minutes, then dripping ammonium persulfate, stirring for 11-13 hours, where 5-sulfosalicylic acid and aniline of mol ratio, the mol ratio of ammonium sulfate and aniline, have the same numerical value, is 4:5-5:4. The solution obtained is filtered form solution with deionized water and ethanol to wash for multiple times until the washing liquid is neutral, vacuum drying the precipitate at 60-70 degrees C for 20-28 hours to obtain graphene oxide/polyaniline composite material. USE - Method of preparing graphene anticorrosive paint for marine environment. DETAILED DESCRIPTION - Preparing graphene anticorrosive paint for marine environment involves dispersing the aniline monomer into the 5-sulfosalicylic acid, ultrasonically processing for 20-40 minutes, adding graphene oxide aqueous solution, stirring for 20-40 minutes, performing ultrasonic dispersion for 20-40 minutes, then dripping ammonium persulfate, stirring for 11-13 hours, where 5-sulfosalicylic acid and aniline of mol ratio, the mol ratio of ammonium sulfate and aniline, have the same numerical value, is 4:5-5:4. The solution obtained is filtered form solution with deionized water and ethanol to wash for multiple times until the washing liquid is neutral, vacuum drying the precipitate at 60-70 degrees C for 20-28 hours to obtain graphene oxide/polyaniline composite material. The separating oil particles whose particle diameter is 5-25nm of nano titanium dioxide is dispersed to a concentration of 0.02-1M of 5-sulfosalicylic acid, followed by adding concentration is 0.25-0.75mg/ml graphene oxide/polyaniline composite solution, continuously stirring for 11-13 hours, centrifuging, centrifugal washing product by distilled water, washing with ethanol and drying to obtain oxidized graphene/polyaniline/titanium dioxide composite nano powder, where the nano titanium dioxide of the graphene oxide/polyaniline composite material whose mass percent is 5-50%. The oxidized graphene/polyaniline/titanium dioxide composite nano-powder, aqueous epoxy resin emulsion and firming agent emulsion, antifoaming agent and de-ionized water, fully stirring, to obtain suspension of anticorrosive paint, where the oxidized graphene/polyaniline/titanium dioxide compositenano-powder weight percentage of anti-corrosive paint is 0.3-5%.