• 专利标题:   High-temperature-resistant and high-strength daily-use ceramic comprises potassium titanate whiskers, talc, corundum powder, oyster shell powder, zinc nitrate, sodium hydroxide, graphene oxide, orange peel and polyvinyl alcohol.
  • 专利号:   CN105906317-A
  • 发明人:   GUO F
  • 专利权人:   GUO F
  • 国际专利分类:   C04B033/132, C04B033/135, C04B033/24
  • 专利详细信息:   CN105906317-A 31 Aug 2016 C04B-033/132 201676 Pages: 5 Chinese
  • 申请详细信息:   CN105906317-A CN10240185 18 Apr 2016
  • 优先权号:   CN10240185

▎ 摘  要

NOVELTY - A high-temperature-resistant and high-strength daily-use ceramic comprises 11-13 pts. wt. potassium titanate whiskers, 15-18 pts. wt. talc, 19-22 pts. wt. corundum powder, 15-19 pts. wt. oyster shell powder, 4-6 pts. wt. zinc nitrate, 0.5-0.6 pt. wt. sodium hydroxide, 13-16 pts. wt. graphene oxide, 0.3-0.5 pt. wt. sodium hexametaphosphate, 40-45 pts. wt. fly ash, 35-40 pts. wt. white glaze balls, 14-17 pts. wt. orange peel, 6-8 pts. wt. shell powder, 4-6 pts. wt. shrimp shell powder, 0.2-0.3 pt. wt. polyvinyl alcohol, 0.2-0.3 pt. wt. tributyl phosphate and deionized water. USE - High-temperature-resistant and high-strength daily-use ceramic (claimed). ADVANTAGE - The ceramic having excellent high-temperature resistance, strength, tear resistance and durability is prepared by simple and economical method. DETAILED DESCRIPTION - A high-temperature-resistant and high-strength daily-use ceramic comprises 11-13 pts. wt. potassium titanate whiskers, 15-18 pts. wt. talc, 19-22 pts. wt. corundum powder, 15-19 pts. wt. oyster shell powder, 4-6 pts. wt. zinc nitrate, 0.5-0.6 pt. wt. sodium hydroxide, 13-16 pts. wt. graphene oxide, 0.3-0.5 pt. wt. sodium hexametaphosphate, 40-45 pts. wt. fly ash, 35-40 pts. wt. white glaze balls, 6-8 pts. wt. waste glass, 4-6 pts. wt. alumina, 8-10 pts. wt. gypsum powder, 10-14 pts. wt. medical stone, 3-4 pts. wt. quartz sand, 21-25 pts. wt. green tea, 14-17 pts. wt. orange peel, 6-8 pts. wt. shell powder, 4-6 pts. wt. shrimp shell powder, 0.2-0.3 pt. wt. polyvinyl alcohol, 0.2-0.3 pt. wt. tributyl phosphate and deionized water. An INDEPENDENT CLAIM is included for preparation of high-temperature-resistant and high-strength daily-use ceramic, which involves mixing potassium titanate whiskers, talc, corundum powder, oyster shell powder, zinc nitrate, sodium hydroxide, graphene oxide, sodium hexametaphosphate, fly ash, white glaze balls, waste glass, alumina, gypsum powder, medical stone, quartz sand, green tea, orange peel, shell powder, shrimp shell powder, polyvinyl alcohol, tributyl phosphate and deionized water to obtain slurry, magnetically processing slurry by magnetic separator, adding slurry to molding machine and drying molded material to form green component, calcining green component and drying product.