• 专利标题:   Preparing pulse current assisted forming graphene-magnesium-based composite material involves using hot-press sintering to prepare graphene-magnesium-based composite material, forming, enhancing shaping performance and compacting structure.
  • 专利号:   CN113174520-A
  • 发明人:   YU Y, ZENG J
  • 专利权人:   UNIV HARBIN SCI TECHNOLOGY
  • 国际专利分类:   C22C023/02, C22C001/05, B22F009/04, B22F003/02, B22F003/14, B22F003/17, C22F001/06, C21D001/40
  • 专利详细信息:   CN113174520-A 27 Jul 2021 C22C-023/02 202170 Pages: 10 Chinese
  • 申请详细信息:   CN113174520-A CN10416601 19 Apr 2021
  • 优先权号:   CN10416601

▎ 摘  要

NOVELTY - Preparing pulse current assisted forming graphene-magnesium-based composite material involves using high energy ball milling-cold pressing-vacuum hot pressing sintering to obtain graphene magnesium-based composite material, applying the pulse current during the rough forming process of the graphene magnesium-based composite material, enhancing its shaping performance without reducing the strength after forming, and making the structure compact. USE - The method is useful for preparing pulse current assisted graphene magnesium-based composite material. ADVANTAGE - The method is economical and has high production efficiency. The composite material has excellent strength and mechanical property.