▎ 摘　　要

NOVELTY - Preparing 24 voltaic graphene conductive wall warm coating comprises (i) taking 5-25 pts. wt. silicone resin, 2-18 pts. wt. graphene, 5-10 pts. wt. antimony pentoxide, 5-12 pts. wt. tungsten oxide, 0.8-1.6 pts. wt. adhesion promoter, 230-250 pts. wt. engineering plastic, 70-80 pts. wt. auxiliary agent, 15-20 pts. wt. cement mortar, and 10- 25 pts. wt. carbon tube, (ii) weighing the raw material parts, adding organic silicon resin, graphene, antimony pentoxide, tungsten oxide, adhesion promoter, engineering plastic, adding auxiliary agent into the stirring device for stirring, the stirring speed is 200-500 rotations/minutes, heating at 60-90℃ to obtain mixed material A, (3) adding cement mortar in the mixing A, carbon tube, mixing and stirring for 1 -6 hours in the stirring device, mixing them uniformly to obtain the coating. USE - The 24-volt graphene conductive wall warm coating is used for electric heating integrated plate used as wall surface, coating layer of paint on surface. ADVANTAGE - The 24-volt graphene conductive wall-warming coating high-temperature rapid baking does not change color, has excellent weather resistance, and can be baked at high temperature of 280℃ without affecting effect. With good compatibility with the resin, does not affect the paint storage stability. DETAILED DESCRIPTION - An INDEPENDENT CLAIM is included for the preparation method of voltaic graphene conductive wall warm coating.