• 专利标题:   Harmless fabric used for clothes, comprises modal yarns, organic yarns and graphene yarns which are woven, where modular yarns are formed in lattice form, and organic yarn is woven with weft yarn, and modal and organic are formed to have thicker thickness than modal.
  • 专利号:   KR2381536-B1
  • 发明人:   LEE J H, OH Y
  • 专利权人:   LEE J H, OH Y
  • 国际专利分类:   D03D001/00, D03D015/20, D03D015/208, D03D015/275, D03D015/283, D06M011/42, D06M011/45, D06M011/47
  • 专利详细信息:   KR2381536-B1 01 Apr 2022 D03D-015/20 202233 Pages: 13
  • 申请详细信息:   KR2381536-B1 KR092335 14 Jul 2021
  • 优先权号:   KR092335

▎ 摘  要

NOVELTY - A harmless fabric comprises a weaved modal yarn, organic yarn, and graphene yarn. The organic yarn is formed to have a thicker thickness than the modal yarn and graphene yarn. The modal, organic and graphene yarns have a UV-protection function by being immersed in a coating mixture comprising 10-12 pts. wt. metal oxide, 0.5-1.5 pts. wt. cellulose, 50-60 pts. wt. alcohol, 45-55 pts. wt. distilled water, and 0.8-1.7 pts. wt. curing agent. The metal oxide comprises 5-15 pts. wt. silver oxide, 2-7 pts. wt. antimony oxide, and 3-9 pts. wt. indium tin oxide. The silver oxide is a silver nanowire having a diameter of 30-45 nm and a length of 25-50 mu m, so that it is attached to surround the harmless fabric and is not peeled from the yarn. The cellulose is used so that the coating mixture is absorbed into the modal yarn, organic yarn and graphene yarn. The curing agent is a silane-coupling curing agent used for curing the coating mixture on the modal yarn, organic yarn and graphene yarn. USE - Harmful fabric is used for clothes. ADVANTAGE - The fabric is harmless to human body, and has good elasticity, processability, flexibility and skin protection effect. The fabric protects the skin and fabric from UV rays through the UV blocking effect by coating the metal oxide on the harmless fabric. DETAILED DESCRIPTION - A harmless fabric comprises a weaved modal yarn, organic yarn and graphene yarn. The modal yarn is formed in a lattice form. The organic yarn is woven with weft and at least one or more organic yarns are spaced apart from each other between the respective weft yarns of the modal yarn formed in the lattice form and are woven into the weft yarn. The graphene yarn is woven with the warp yarn. At least one or more graphene yarns are spaced apart from each other at a certain interval between each warp of the modal yarn formed in the lattice form and woven in a warp. The organic yarn is formed to have a thicker thickness than the modal yarn and graphene yarn to protrude than the modal yarn and graphene yarn. The modal yarn, organic yarn and graphene yarn have a UV-protection function by being immersed in a coating mixture comprising 10-12 pts. wt. metal oxide, 0.5-1.5 pts. wt. cellulose, 50-60 pts. wt. alcohol, 45-55 pts. wt. distilled water, and 0.8-1.7 pts. wt. curing agent. The metal oxide comprises 5-15 pts. wt. silver oxide, 2-7 pts. wt. antimony oxide, and 3-9 pts. wt. indium tin oxide. The silver oxide is a silver nanowire having a diameter of 30-45 nm and a length of 25-50 mu m, so that it is attached to surround the harmless fabric and is not peeled from the yarn. The cellulose is used so that the coating mixture is absorbed into the modal yarn, organic yarn and graphene yarn. The curing agent is a silane-coupling curing agent used for curing the coating mixture on the modal yarn, organic yarn and graphene yarn.