▎ 摘　　要

NOVELTY - Modified asphalt paint comprises epoxy resin E12, polycarbodiimide, polyether ester, graphene, nickel-doped titanium dioxide, cobalt naphthenate, dimer acid, cycloaliphatic amine, cardanol, toluene glycidyl ether, abandoned modified silicate sand, modified asphalt, wood wax oil, hexabromobenzene, polyvinylether, xylene, ethylene glycol, aluminum methylbutyl phosphinate, and talcum powder. The modified asphalt comprises e.g. asphalt, aluminum stearate, C9 petroleum resin, carboxymethylcellulose, thermoplastic elastomer, nano-montmorillonite powder, polyethylene wax, and octyl phthalate. USE - The modified asphalt paint is useful for ship (claimed). ADVANTAGE - The modified asphalt paint can be economically produced with increased temperature resistance, high flame retardant property, and improved weather resistance, corrosion resistance, moisture resistance and water resistance. DETAILED DESCRIPTION - Modified asphalt paint comprises 32-35 pts. wt. epoxy resin E12, 1-2 pts. wt. polycarbodiimide, 1-2 pts. wt. polyether ester, 3-4 pts. wt. graphene, 1-2 pts. wt. nickel-doped titanium dioxide, 0.3-0.7 pts. wt. cobalt naphthenate, 1-2 pts. wt. dimer acid, 2-4 pts. wt. cycloaliphatic amine, 2-3 pts. wt. cardanol, 2-4 pts. wt. toluene glycidyl ether, 8-13 pts. wt. abandoned modified silicate sand, 9-14 pts. wt. modified asphalt, 3-5 pts. wt. wood wax oil, 1-2 pts. wt. hexabromobenzene, 2-3 pts. wt. polyvinylether, 8-11 pts. wt. xylene, 6-9 pts. wt. ethylene glycol, 0.5-1 pts. wt. aluminum methylbutyl phosphinate, and 1-2 pts. wt. talcum powder. The modified asphalt comprises 80-84 pts. wt. asphalt, 0.3-0.6 pts. wt. aluminum stearate, 4-6 pts. wt. C9 petroleum resin, 1-2 pts. wt. carboxymethylcellulose, 0.4-0.8 pts. wt. thermoplastic elastomer, 1-2 pts. wt. nano-montmorillonite powder, 0.3-0.6 pts. wt. polyethylene wax, 0.3-0.6 pts. wt. octyl phthalate, 0.5-1 pts. wt. rosin glycerin ester, 0.3-0.7 pts. wt. zinc ethylhexanoate, 1-2 pts. wt. asbestos fibers, 0.5-1 pts. wt. polyoxyethylene fatty alcohol ether, 7-9 pts. wt. linseed oil, 0.5-1 pts. wt. maleic acid, 12-15 pts. wt. water, and 2-3 pts. wt. acetic acid butyl ester, and is prepared by mixing maleic acid and linseed oil, heating at 160-190 degrees C to obtain modified linseed oil, heating the asphalt at 150-190 degrees C, performing a high speed centrifuging, cutting and grinding into a size of 10-30 mu m, uniformly mixing polyoxyethylene fatty alcohol ether, aluminum stearate, thermoplastic elastomer, nano-montmorillonite powder and C9 petroleum resin with water, heating to 60-90 degrees C to form mixed solution, mixing modified linseed oil and mixed asphalt solution, grinding and dispersing for 20 minutes, adding the rest of residual substance, and grinding for 20-30 minutes to obtain the product. An INDEPENDENT CLAIM is included for abandoned modified silicate sand prepared by adding waste water glass sand to a roaster, calcining at 150-200 degrees C for 1-2 hours, adding the waste water glass sand to a heated rotary grinding device, high speed grinding, performing ultrasonic vibration for 2-3 hours, washing with water, drying, adding 17% of sepiolite, 4% of carbon black and 7% alumina to the waste water glass sand, grinding to 400-600 mesh powder, adding 0.5-1 wt.% of n-butyl titanate to waste water glass sand, and evenly grinding.