• 专利标题:   Preparation of carbon nanotube graphene inorganic zinc-rich anticorrosive coating used in e.g. marine engineering, involves preparing main agent by using graphene, carbon nanotubes, zinc powder, toluene, and n-butanol.
  • 专利号:   CN108864931-A
  • 发明人:   ZHOU Y
  • 专利权人:   FOSHAN CHANCHENG RELA SPACE BIOTECHNOLOG
  • 国际专利分类:   C09D179/02, C09D163/00, C09D005/10, C09D005/24
  • 专利详细信息:   CN108864931-A 23 Nov 2018 C09D-179/02 201907 Pages: 4 Chinese
  • 申请详细信息:   CN108864931-A CN10807311 21 Jul 2018
  • 优先权号:   CN10807311

▎ 摘  要

NOVELTY - The preparation of carbon nanotube graphene inorganic zinc-rich anticorrosive coating involves grinding carbon nanotubes into powder, dissolving graphene, dissolving powdered carbon nanotubes and zinc powder in organic solvent of toluene and n-butanol, stirring using a high speed disperser (I) to obtain main agent, adding polyaniline to the beaker, adding toluene and n-butanol to the beaker, stirring for 15 minutes, adding epoxy resin into beaker, continuously adding toluene and n-butanol in beaker for 15 minutes, pouring the solution into high-speed disperser (II), stirring for 45 minutes, and adding pyridine to obtain additive, placing main agent and additive in a mixer, mixing, stirring for 15 minutes, adding pyridine during stirring, adding T-31 fixative after stirring is completed, stirring vigorously for 5 minutes, and placing paint in a vacuum oven for 15 minutes to remove air bubbles after the fixing agent and the solution are evenly mixed. USE - Preparation of carbon nanotube graphene inorganic zinc-rich anticorrosive coating used in marine engineering, transportation, and municipal engineering application. ADVANTAGE - The method enables preparation of carbon nanotube graphene inorganic zinc-rich anticorrosive coating with high strength, high tribological properties, high conductivity, excellent salt spray resistance, strong adhesion force, excellent wear resistance, excellent water resistance, high hardness, reduces the thickness of the coating, and increases adhesion to the substrate.