• 专利标题:   Preparation of graphene/polybutylene succinate composite material, involves dissolving polybutylene succinate in solvent to form solution, and dispersing graphene in solvent to form solution.
  • 专利号:   CN106243643-A, CN106243643-B
  • 发明人:   HUANG J, CUI C
  • 专利权人:   UNIV NINGDE NORMAL, UNIV NINGDE NORMAL
  • 国际专利分类:   B29B007/72, C08K003/04, C08L067/02
  • 专利详细信息:   CN106243643-A 21 Dec 2016 C08L-067/02 201714 Pages: 8 Chinese
  • 申请详细信息:   CN106243643-A CN10689118 19 Aug 2016
  • 优先权号:   CN10689118

▎ 摘  要

NOVELTY - The preparation method of graphene/polybutylene succinate composite material involves (i) dissolving polybutylene succinate in a solvent (a) to form a solution (a), (ii) dispersing graphene in solvent (a) to form a solution (b), (iii) mixing solution (a) and solution (b) to form a mixed solution, (iv) pouring mixed solution into a solvent, precipitating polybutylene succinate, (v) removing the solvent (a) and solvent (b) in reaction product, (vi) roll-coating the product by a two-roll mill, and gradually reducing the roller temperature. USE - Preparation of graphene/polybutylene succinate composite material (claimed). DETAILED DESCRIPTION - The preparation method of graphene/polybutylene succinate composite material involves (i) dissolving polybutylene succinate in a solvent (a) to form a solution (a), (ii) uniformly dispersing the graphene in solvent (a) to form a solution (b), (iii) uniformly mixing solution (a) and solution (b) to form a mixed solution, (iv) pouring mixed solution into a solvent, precipitating polybutylene succinate, where polybutylene succinate is insoluble or sparingly soluble in solvent (b), (v) removing the solvent (a) and solvent (b) in reaction product, (vi) roll-coating the product by a two-roll mill at 120 degrees C, and gradually reducing the roller temperature to 90 degrees C, until the surface of film is smooth and uniform.