▎ 摘　　要

NOVELTY - Solution of resin balls and solution of alkene-graphene oxide are mixed and magnetically stirred, to obtain mixed solution. The mixed solution is ultrasonically processed, to obtain solution of alkene-graphene oxide resin balls. The solution of alkene-graphene oxide resin balls is filtered, and the obtained residue is air-dried, to obtain alkene-graphene oxide resin ball powder. The alkene-graphene oxide resin ball powder is reduced by being exposed to flash lamp, and the resin surface of ball is covered with graphene oxide, to obtain alkenyl-graphene oxide resin balls. USE - Preparation of graphite alkenyl resin used for preparing electroconductive frame adhesive (claimed). ADVANTAGE - The method enables economical preparation of graphite alkenyl resin with high yield by simple method. DETAILED DESCRIPTION - 0.1-5 mg/ml Solution of resin balls and 1-10 mg/ml solution of alkene-graphene oxide are mixed and magnetically stirred for 5 minutes to 1 hour, to obtain mixed solution. The mixed solution is ultrasonically processed for 5 minutes to 2 hours, to obtain solution of alkene-graphene oxide resin balls. The solution of alkene-graphene oxide resin balls is filtered, and the obtained residue is air-dried at 60-100 degrees C for 0.5-4 hours, and moisture is completely-removed, to obtain alkene-graphene oxide resin ball powder. The alkene-graphene oxide resin ball powder is reduced by being exposed to flash lamp, and the resin surface of ball is covered with alkene-graphene oxide, to obtain alkenyl-graphene oxide resin balls. An INDEPENDENT CLAIM is included for preparation of electroconductive frame adhesive.